Phrozen High Speed PLA 1kg White

This premium quality will wow you with it's great results and speed you can print at. Key features are:

• Benefits

  • Fast Printing Speed: Complete your prints in a shorter time when used together with Phrozen Arco.
  • Maintain Quality Even at High Speed: With outstanding fluidity, Phrozen High-Speed PLA facilitates faster and smoother extrusion with quicker cooling for high-quality prints.
  • Best Bang for Your Buck: Whether you are a seasoned 3D printing enthusiast or a beginner dipping your toes into FDM 3D printing, the Phrozen High-Speed PLA is an affordable option to kickstart your journey on the right foot.

  Specs

  • Density: 1.2—1.25g/cm2
  • Tensile Strength (MPa): 55+/-10%
  • Tensile Modulus (MPa): 1200 +/-10%
  • Elongation at Break (%): 10.2 +/-10%
  • Bending Strength (MPa): 70 +/-10%
  • Bending Modulus (MPa): 1606 +/-10%
  • Impact Strength (J/m): 50+/-10%
  • Shrinkage Rate: 0.5%
  • Heat Deflection Temperature (@0.45MPa): 50°C
  • MFI (Melt Flow Index): 10.68g/10min
  • Nozzle Temperature: 190-220°C
  • Bed Temperature (PEI Plate): 45~60°C
  • Printing Speed: Up to 600 mm/s

  
  

  Precautions

  • Please operate at room temperature in a cool, well-ventilated area.
  • The material is hygroscopic; when not in use, please seal well and store in a dry environment to prevent moisture absorption.
  • When the material has been opened for a long time, it is recommended to bake it before printing.
  • If warping occurs during printing, please increase the heated bed temperature as recommended.
  • The nozzle is prone to clogging. Evaluate cleaning or filament replacement if extrusion is not smooth.
  • For personal safety, it's recommended to wear a mask during printing operations to prevent the inhalation of airborne particles that may be generated during the process.
  • Please dispose of waste according to recycling procedures for "general resource materials" in your local area.
  • The shelf life is one year; once opened, please use it up as soon as possible.